FRP Rods produced by our company has applied the pultrusion process technology, of which high-quality raw materials of reinforcedglass fibers and epoxy resin are used.
| Diameter (mm) | Kg/Mtr | Diameter (mm) | Kg/Mtr | Diameter (mm) | Kg/Mtr |
|---|---|---|---|---|---|
| 8 | 0.116 | 24 | 0.96 | 45 | 3.37 |
| 10 | 0.176 | 26 | 1.04 | 48 | 3.83 |
| 12 | 0.24 | 28 | 1.305 | 50 | 4.16 |
| 16 | 0.43 | 30 | 1.5 | 53 | 4.67 |
| 17 | 0.481 | 32 | 1.728 | 60 | 5.99 |
| 18 | 0.54 | 35 | 2.04 | 70 | 8.15 |
|---|---|---|---|---|---|
| 19 | 0.6 | 36 | 2.16 | 80 | 10.65 |
| 20 | 0.67 | 38 | 2.4 | 90 | 13.48 |
| 22 | 0.805 | 40 | 2.66 | 110 | 20.327 |
| Item | Unit | Values | Standard |
|---|---|---|---|
| Density (20±2) | g/cm 3 | ≥2.1 | ASTM D 792 |
| Water Absorption Rate | % | ≤0.05 | ASTM D 570 |
| Tesile Strength | Mpa | 1420 | ASTM D 638 |
| Bending Strength | Mpa | 900 | ASTM D 790 |
| Torsional Strength | N/mm 2 | ≥90 | ASTM D 4923 |
| Thermal Bending Strength | Mpa | ≥300 | ASTM D 790 |
| Dye Penetration Test | min | ≥15 | ASTM D 5117 |
| Volume Resistivity (140, 96h) | Ω·m | ≥10 10 | ASTM D 257 |
| Water Diffusion Test 0.1% Nacl, 100h, 12 kV, 1min | mA | ＜0.03 | IEC 1109 |
| Lightning Impulse Withstand Voltage (100kv) | times | ≥5 | ASTM D 149 |
| DC breakdown voltage | kV | ≥50 | ASTM D 149 |
| Heat deflection temperature | ≥135 | ASTM D 648 | |
| Glass Fiber Content | % | 70-80 | ASTM D 2584 |